Phosphorous Pentoxide Producing Methods

ABSTRACT

A phosphorous pentoxide producing method includes forming a kiln bed using feed agglomerates with a calcium-to-silica mole ratio of from 0.5 to 1.0 and maintaining a bed temperature at or above 1260° C. along a portion of the bed length without exceeding 1380° C. along the entire bed length. Less than 10% of the agglomerates&#39; phosphate input to the kiln remains in the kiln residue as phosphate. Another method includes maintaining a bed temperature at or above 1180° C. along a portion of the bed length and establishing a bed surface-to-volume ratio multiplied by a time for bed heat up to 1180° C. of less than 50 minutes-ft 2 /ft 3 .

RELATED APPLICATION DATA

This application is a continuation-in-part of U.S. patent application Ser. No. 12/125,751, filed May 22, 2008, and entitled “Phosphorous Pentoxide Producing Methods,” which is a continuation of U.S. patent application Ser. No. 11/818,115, incorporated herein by reference and filed Jun. 13, 2007, now U.S. Pat. No. 7,378,070, which is a continuation-in-part of U.S. patent application Ser. No. 11/330,034, filed Jan. 11, 2006, which is a continuation-in-part of U.S. patent application Ser. No. 11/145,564, filed Jun. 3, 2005, which claims the benefit of U.S. Provisional Application No. 60/648,360, filed Jan. 28, 2005, and U.S. Provisional Application No. 60/577,286, filed Jun. 4, 2004.

TECHNICAL FIELD

The invention pertains to methods for producing phosphorous pentoxide performed in counter-current rotary kilns.

BACKGROUND OF THE INVENTION

One known method for producing phosphorous pentoxide (P₂O₅, usually present as the dimer P₄O₁₀ in the gas phase) involves processing raw material agglomerates containing phosphate ore, silica, and coke in the bed of a rotary kiln to chemically reduce the phosphate ore and generate gaseous phosphorus metal (P₄) and carbon monoxide (CO) off gas to the kiln freeboard where they are burned (oxidized) with air to provide heat for the process. It may be referred to as the kiln phosphoric acid (KPA) process. The oxidized phosphorus metal is a phosphorus oxide (normally, P₄O₁₀) which can be scrubbed from the kiln off gases with a phosphoric acid (H₃PO₄) solution and water to make a suitable phosphoric acid product.

KPA process chemistry is similar to another process known as the furnace acid process for manufacture of phosphoric acid. In the furnace process, the raw materials are heated and partially melted. An endothermic reduction reaction is carried out in one vessel called the electric furnace where the heat is supplied by the use of electric resistance heating in the bed. The phosphorus metal is recovered from the off gas of the furnace with cold water sprays as liquid phosphorus metal which can be transported to another vessel called the burner where it generates considerable heat while being burned with air. The resulting phosphorus oxide is absorbed in water to make a concentrated, high purity phosphoric acid.

The electric furnace in the furnace process does not use the heat generated from burning phosphorus metal that arises in the burner vessel. Also, the electric furnace does not use heat from burning the carbon monoxide that it generates. Although widely used in the last century for producing phosphoric acid, the cost of electricity as compared to the cost of sulfuric acid resulted in shutdown of most of the furnace acid plants in favor of another process known as the sulfuric acid process for making phosphoric acid.

If the heat generated in burning the off gasses from the furnace process reduction reaction could be utilized to provide the heat requirements of the reduction process, thereby replacing electrical heating, then economies might be realized. Converting the furnace process carbon reductant to carbon dioxide might generate sufficient heat, if used efficiently, to replace all the heat added by electricity in the furnace process. A vision of such potential motivated many researchers over the years to develop concepts where heat integration could be realized. The following references describe the various attempts: Levermore (U.S. Pat. No. 2,075,212), Lapple (U.S. Pat. Nos. 3,235,330 and 3,241,917), Saeman (U.S. Pat. No. 3,558,114), Megy (U.S. Pat. Nos. 4,351,809 and 4,351,813), Hard (U.S. Pat. Nos. 4,389,384), and Park (U.S. Pat. No. 4,420,466). All of the described processes use a rotary kiln with a reducing bed and an oxidizing freeboard and are collectively within the realm of KPA processes.

A kiln within a kiln concept forwarded in the Levermore patent addressed the heat integration issue in a reasonable conceptual way, but was not practical because no material of construction for the inner kiln was available. The Levermore process heated up the agglomerated solids containing phosphate ore, silica, and carbonaceous material and conducted the endothermic reduction reaction in an inner kiln held inside an outer kiln. The P₄ and CO off gases from the reduction reaction in the inner kiln passed between the outside wall of the inner kiln and the inner wall of the outer kiln, where air was admitted to oxidize the P₄ and CO, generating sufficient heat to supply the requirements of the inner kiln. The heat then passed through the outside wall of the inner kiln.

The Lapple and Megy patents recognized that a separate oxidizing freeboard and reducing bed could be maintained in a kiln without a separating wall, but failed because of melting problems during the phosphate reduction reaction. Lapple and Megy specify a calcium-to-silica mole ratio in the feed to the kiln greater than 1.0.

The Park patent describes a process requiring ore with less silica than is cheaply available and a very hot kiln operation that has not appeared attractive enough to encourage commercialization to date.

The process in the Saeman patent involves carrying out the rotary kiln reduction reaction in a molten slurry, contained within the shell of the kiln protected by freezing a layer of solids on the inside of the kiln wall. This process has been abandoned.

The process in the Hard patent showed promise and a continuous pilot plant based on a 33 inch diameter by 30 feet long kiln was operated under the direction of the present inventor in the early 1980's. The results were published in Leder, et al., A New Process for Technical Grade Phosphoric Acid, Ind. Eng. Chem. Process Des. Dev., 1985, 24, 888-897, but the process was abandoned as his teachings were not complete enough to show how to carry out an economic commercial process. The pilot plant yields were low, with a maximum yield of 72% when run in a commercial mode without bedding coke, and 86% when a large amount of bedding coke was used. Other problems included: 1) throughput rates that were low which indicated a high capital cost requirement for the process, 2) high temperature of operation (greater than 1435° C.) to reach high yields, which put the operation close to melting problems and required higher silica admixtures in the kiln feed than desired for commercial operation, and 3) high maintenance problems. The high temperature and partial oxidation of carbon from the kiln solids resulted in transfer of significant amounts of fluorine, sodium, potassium, and sulfur to the kiln off gas, producing deposits in the back end of the kiln and off gas lines, contamination of the product acid, and extra costs associated in scrubbing acidic gases from the process. The off gases from the process were reducing requiring the added cost of an after burner. The combination of these problems was such that no one has attempted to commercialize the Hard process even though it has now been over twenty years since the pilot plant was operated.

As may be appreciated from the previous difficulties described above, the KPA process may be improved further.

Phosphoric acid may also be produced using the wet acid process, which has been used with phosphate ore and sulfuric acid commercially since approximately 1842. The process yields an impure, black phosphoric acid solution with about 26% P₂O₅ that is concentrated to make solid fertilizers (diammonium phosphate [DAP] and monoammonium phosphate [MAP]) or further processed to make super phosphoric acid (SPA) used for liquid fertilizers. The solution can also be further purified by solvent extraction to make a technical grade acid for various industrial markets. The wet acid process has been the dominant manufacturing method for producing phosphoric acid, except for a period during the last century when the electric furnace acid process produced nearly as much phosphoric acid as the wet acid process. However, the wet acid process makes a weak and impure grade of phosphoric acid.

Of particular concern are the magnesium, aluminum, iron, sodium and potassium impurities contained as significant minor impurities in the phosphate ore used as a raw material for the wet acid process. Essentially, the sulfuric acid renders the impurities soluble so that most of the weight of impurities report to the weak phosphoric acid of 26-28% P₂O₅ content typically produced from the wet acid process.

Prior to the manufacture of solid phosphate fertilizers some of the impurities are removed by concentrating the phosphoric acid by evaporation to first about 42% P₂O₅ and then about 54% P₂O₅. At both stages of evaporation, a significant amount of sludge drops out rich in impurities. At 42%, most of the sludge is calcium sulfate and includes some lost phosphate. At 54%, most of the sludge is magnesium aluminum phosphate and includes some other lost phosphates. The sludges are removed by filtration and frequently used to make low grade fertilizer products.

The 54% acid called “Merchant Grade Acid” still contains most of the weight of impurities from the ore (about 70% of the magnesium) and is then used to make solid fertilizers by a process called granulation, typically by reacting with ammonia to make MAP and DAP. If the impurities in the phosphate ore are above an upper limit, particularly with respect to magnesium, then the granulated MAP and DAP may not meet specifications for commercial products. These inferior products may be sold at a discounted price.

As may be appreciated from the previous difficulties described above, the materials used to make fertilizers may also be improved further.

BRIEF DESCRIPTION OF THE DRAWINGS

Preferred embodiments of the invention are described below with reference to the following accompanying drawings.

FIG. 1 is a block diagram of a KPA process according to one aspect of the invention.

FIG. 2 is a chart pertaining to Example 1 showing melting temperatures with respect to calcium-to-silica mole ratio and showing the temperatures for greater than 92% yield in 1, 2, and 4 hours with respect to calcium-to-silica mole ratio.

FIG. 3 is a chart showing volatility for various elements with respect to temperature.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Through research and development of the KPA process, observation, study, and insight resulted in several process improvements which overcome deficiencies of the processes described in Hard and other references mentioned in the Background section above. Various aspects of the present invention provide for high yields of phosphoric acid, efficient use of carbonaceous raw material requirements, high kiln throughputs, long refractory life, limited sinoite (Si₂N₂O) formation, oxidizing off gas, and the capability of limiting sodium, potassium, fluorine, and sulfur loss from the kiln solids.

Efforts now confirm that the yield limitations present in the Hard continuous pilot plant resulted primarily from burn out of carbon in a shell that formed on the outside portion of the agglomerate as it heated up to greater than 1180° C., at which temperature the phosphate ore reduction began. The carbon burned out (oxidized) from the outside surface of the ball by reaction with oxidizing gases from the kiln freeboard (e.g., CO₂, P₄O₁₀, and H₂O). Assuming an agglomerate was in the form of a 1.0 centimeter ball and 30 weight % (wt %) of the carbon was burned out, then a white shell about 800 micrometers thick formed on the outside of the ball. The phosphate ore in the shell was not reduced, even after reaching reaction temperature as there was no carbon therein to reduce it, and yield was limited.

Also, sodium, potassium, sulfur and fluorine were largely volatilized from the shell, but were retained in the core containing residual carbon. Thus, limiting carbon burnout may reduce loss of sodium, potassium, sulfur and fluorine from the bed.

As a result of the research described herein, it was newly discovered that after phosphate reduction begins and the phosphorus metal vapor begins to form in the core of an agglomerate, phosphorous metal may encounter oxidizing gases either in the oxidized shell of the ball or in the bed between the balls. The P₄ emerging from the core may oxidize into P₄O₁₀ which may react with the unreacted phosphate ore in the shell to form calcium metaphosphate. Calcium metaphosphate has a melting point of 973° C. (which is below the reduction temperature) and is stable against disproportionation to calcium pyrophosphate and P₄O₁₀ at kiln temperatures, provided the vapor pressure of P₄O₁₀ is greater than 1 millimeter of mercury. Such formation of calcium metaphosphate likely further limited yield in the Hard process beyond yield loss directly associated with carbon burnout.

However, efforts taken to limit carbon burnout may also decrease the transfer of P₄O₁₀ to the bed and, therefore, decrease P₄O₁₀ reaction with ore and formation of calcium metaphosphate. Thus, it becomes doubly important to reduce carbon burnout from the bed in order to limit the indicated back reaction, further improving yield and also retaining more sodium, potassium, sulfur and fluorine otherwise lost from the bed.

If the phosphorus metal vapor and associated carbon monoxide from the reduction reaction evolve fast enough, then they sweep the oxidizing gases away from the bed and limit further oxidation of the carbon from the bed. The vigor of the evolution is directly related to the bed surface-to-volume ratio. In sufficiently large kilns, the carbon burnout is effectively stopped during the period when the phosphorus reduction reaction is occurring. Once the reduction reaction occurs, the solid reaction product includes an amorphous (glassy) calcium metasilicate (CaSiO₃) which encapsulates any remaining carbon, protecting it from further oxidation.

Since loss of carbon from the ball by carbon burnout may lead to a reduction in yield, limiting the carbon burnout to low levels may provide high yields. Control of carbon burnout may be achieved primarily by implementing one or more of the following measures, which are additive in their effect in reducing carbon burnout:

1) Reducing surface-to-volume ratio of the kiln bed.

2) Using a control system which includes air ports down the length of the kiln to introduce over bed air at a controlled rate to provide for a rapid heating of the kiln feed to the temperature where the phosphate reduction reaction proceeds (i.e. greater than 1180° C.) and maintaining the reduction temperature over most of the length of the kiln.

3) Using appropriate kiln design to reduce turbulence in the region of the kiln where the kiln solids heat up from 700 to 1180° C., where the phosphate reduction reaction begins.

4) Using uncalcined carbonaceous raw material to provide an off gas of hydrocarbons during the heating of the kiln feed to reaction temperature to blanket the bed in reducing gasses and to react with oxidizing gasses.

5) Using finely ground and intimately mixed carbonaceous material in the feed agglomerates to lower the temperature of full phosphate reduction at commercial feed rates to about 1180° C.

6) Adding a small, but sufficient, amount of uncalcined carbonaceous raw material together with the kiln feed agglomerates as bedding to preferentially react with incoming oxidizing gases, particularly phosphorus oxide, from the freeboard.

According to one aspect of the invention, a phosphorous pentoxide producing method includes forming a kiln bed using feed agglomerates in a counter-current rotary kiln, the bed having a length and the agglomerates containing phosphate ore particles, carbonaceous material particles, and sufficient silica particles for the agglomerates to exhibit a calcium-to-silica mole ratio of less than 1.0. The method includes maintaining a bed temperature at or above 1180° C. along at least 50% of the bed length without exceeding 1380° C. along the entire bed length. Kiln off gas is generated and phosphorous pentoxide is collected from the kiln off gas, the kiln discharging a residue containing processed agglomerates and less than 10% of the agglomerates' phosphate input to the kiln remaining in the residue as phosphate.

As a result of the research described herein, it was newly discovered that reducing bed surface-to-volume ratio perhaps provides the most significant benefit, particularly in combination with the use of uncalcined petroleum coke or coal as the carbonaceous raw material source in the agglomerates. To process a given bed volume, a stoichiometric amount of oxygen is provided to generate sufficient heat in the off gas to run the process. Supplying the oxygen from air moves a specific volume of kiln freeboard gases countercurrent to the kiln solids.

In scaling up, commercially-sized kilns normally exceed a minimum diameter above which kiln shell heat losses become minor. The cross-sectional area of the bed and freeboard both scale up with the square of the diameter of the kiln. Since bed cross-sectional area is directly proportional to kiln diameter squared, so is the bed volume, the stoichiometric amount of oxygen for the bed volume, and the corresponding specific volume of freeboard gases from the air that provides the oxygen. However, the cross-sectional area of the freeboard also is directly proportional to kiln diameter squared, so the velocity of the gas flowing countercurrent to the kiln solids is independent of kiln diameter at a given temperature of operation.

Since the gas velocity relative to the kiln solids is about the same, the turbulence is about the same and the transfer of oxidizing gases from the freeboard into the bed is about the same regardless of kiln diameter, provided the configuration of the kiln is the same. The kiln may include dams to better control the depth of the solids over the kiln length, especially when increased bed volume is desired. The dams may have a long, tapered approach to limit the turbulence that may otherwise result from their use.

The surface area available for heat transfer from the freeboard gasses to the kiln solids in the bed is directly proportional to the length of the kiln. If stoichiometric air is used to oxidize the phosphorus, carbon monoxide and hydrocarbons from the bed, then the total flow of gas in the kiln increases for an increased bed volume. Thus, the gas velocity in the kiln is directly proportional to the kiln length.

Long kilns are used in heat transfer processes to maximize heat utilization in processes like wet process cement production etc. In a KPA process, a stoichiometric amount of carbon is used to reduce the phosphorus from the bed. The reduction produces a specific amount of combustibles from the bed which, when oxidized with air, give a modest excess of heat in the kiln. The excess heat gives a kiln off gas temperature higher than would be required. A direct result is that a kiln suitable for the KPA process may be shorter rather than longer. The shorter kiln presents a condition that also benefits carbon burnout as the freeboard gas velocity is reduced. Thus, in the KPA process, the carbon burnout rate increases in longer kilns as the freeboard gas velocity increases.

Evaluation of three data sources provided the carbon burnout in batch and commercial kilns. As the first source, sufficient data is available in Folmo et al., Ilmenite Direct Reduction Project in Norway using the GRATE-CAR™ Process, AIME Conference, 1992, supplemented by information from Allis Chalmers engineers that started up the facility. The data pertains to carbon burnout rate in a 19 feet diameter by 232 feet long reducing kiln processing ilmenite ore in Tyssedal, Norway since 1986 to produce metallic iron and a higher value TiO₂ residue. The kiln solids were held at about 1170° C. and the carbon burnout was about 1.1 pound per hour per square foot. Although not enough data is given in the Folmo article to estimate the freeboard velocity, the kiln was a bit elongated, which probably resulted in a freeboard gas flow rate of perhaps 25 feet per second, as is common in kilns of its shape.

As the second source, in the Leder article discussed in the Background section above, the temperature of the kiln bed averaged about 1200° C. over the length where the carbon burnout was determined to average in the range of 0.2 to 0.3 pounds per hour per square foot. The gas velocity in this much shorter kiln averaged about 3.3 feet per second.

As the third source, a 13.5 inch batch kiln used in Example 3 described below was determined carefully to produce carbon burnout of about 2 pounds per hour per square foot during the time the solids were heating to reaction temperature.

The first observation that can be made from the above data involves the burn out of carbon as a first approximation being directly related to the surface area of the kiln bed, which in turn is directly related to the diameter of the kiln and the length of the kiln. In the two continuous kiln systems above, the amount of surface in the kiln systems changes by a factor of 55, but the carbon burnout only by a factor of 3-4. Most of the higher burnout rate in the larger kiln is due to the increased flow rate of the freeboard gasses.

The carbon burnout rate in the batch kiln is a factor of 7-10 higher than the continuous kiln even though the “apparent” freeboard gas velocity is only 0.44 feet per second. The batch kiln is closed with a perpendicular lid with a 9 inch hole in it. In fact all of the kiln gases exit through the relatively small hole at an exit velocity of about 5 feet per second. The gas flow through the relatively small hole entrains other gas in the kiln that diverges toward the bed as it hits the lid, setting up a strong recycle gas flow. When this gas flow hits the bed at the lower portion of the lid, it impinges directly on the surface of the bed and the momentum drives the oxidizing gases directly into the bed, resulting in enhanced carbon burnout. The high turbulence in the batch kiln causes high carbon burnout and limits high yield in reduction processes in the batch kiln. The batch kiln represents the standard tool commonly used in the development of kiln processes. The enhanced burnout associated with the turbulence in the batch kiln apparently led researchers to underestimate the prospects for reducing bed processes.

In a continuous kiln operated as previously known, the feed agglomerates enter at about 125° C., and are well away from the inlet end of the kiln by the time they reach the temperature of 700° C. where the carbon burns out of the bed fast enough to be of concern to the process. At that point, the gases in the kiln flow smoothly over the kiln solids with minimum turbulence. In aspects of the present invention, increased turbulence might be reduced by tapering the ends of the kiln rather than using an abrupt dam to retain solids in the bed.

The amount of carbon present in the kiln bed relates to the volume of the bed, which relates to the square of the diameter of the kiln. The carbon burnout is proportional to the surface area which relates to the first power of the diameter of the kiln. Therefore, the fraction of carbon which burns out of the kiln bed directly relates to the inverse of the diameter of the kiln. As shown in Example 3 below, the magnitude of the rate of carbon burnout is such that in a small batch kiln (e.g., 13.5 inch diameter batch kiln) it is difficult to have any carbon left in the kiln solids after heating them to reaction temperature. In large, continuous kilns a much greater fraction of the carbon remains in the kiln solids.

Another factor that directly affects the amount of carbon burnout is how long the kiln solids are exposed to oxidizing freeboard gases as they heat up to reaction temperature. In the KPA process, rapidly heating the feed agglomerates to reaction temperature involves a means of oxidizing part of the phosphorus and carbon monoxide off gases from the phosphate reduction reaction down the length of the kiln using the kiln control system described below for FIG. 1 and/or Example 5.

In a 6 foot diameter continuous pilot plant kiln (72 feet long) designed for low turbulence, a kiln system with the ratio of bed surface-to-volume multiplied by the bed heat up time of less than 50 minutes-ft²/ft³ may obtain yields greater than 92% with high throughput, low impurity volatilization, extended refractory life, and elimination of the competing sinoite reaction described below. As explained below in further detail, larger diameter kilns of greater than 12 feet operating under otherwise identical conditions may provide greater yields, for example, greater than 95%.

In combination with the use of uncalcined carbonaceous material in the feed agglomerates, surface/volume ratio in the kiln bed provides even more benefit. Uncalcined carbonaceous material decomposes when heating to form gaseous hydrocarbons (mostly methane) and a stable carbon residue known in the industry as “fixed carbon,” which does not volatilize at process temperatures and is the reactant used to reduce the phosphate ore. The volatiles in carbonaceous components of phosphate ore and coal begin to evolve as soon as the feed agglomerates are heated above room temperature. Green petroleum coke, having already been subjected to coking temperatures, may begin evolving hydrocarbons at about 600° C. Most of the carbonaceous materials finish evolving their hydrocarbons by about 950° C.

During bed heat up, oxidation of fixed carbon by air at a significant rate typically does not occur until reaching temperatures above about 700° C., well after the volatiles from green petroleum coke in kiln solids begin to exert their protective effect at about 600° C. Even so, transfer of P₄O₁₀ to the bed may occur from the time the solids enter the kiln until they reach reaction temperature. Thus, the time it takes to bring the kiln solids from kiln inlet to 1180° C. defines “heat up time” in the context of the present document, unless otherwise indicated. However, it is clear that the availability of uncalcined carbonaceous material in the kiln solids makes the process somewhat more tolerant to a slower kiln solids heat up rate.

During the vulnerable period when feed agglomerates are being heated to reaction temperature, observation indicates that volatilization of gaseous hydrocarbons provides a gas sweep, significantly limiting the transport of oxidizing species from the kiln freeboard to the kiln bed. The extent of the hydrocarbon gas sweep is directly proportional to the diameter of the kiln. That is, the amount of volatiles present in the bed is directly proportional to the volume of the bed (i.e. the square of the diameter of the kiln) while the area that the volatiles come out of the bed is proportional to the area of the bed (i.e. the diameter of the kiln). Thus, the flux of hydrocarbons from the surface of the bed is directly proportional to the diameter of the kiln.

However, the amount of volatiles in green petroleum coke is on the order of ten times less than the amount of phosphorus metal and carbon monoxide formed after a given volume of agglomerates reaches 1180° C. Therefore, the effectiveness in sweeping away oxidizing gasses from the freeboard increases with the scale up of the kiln to larger diameters, making commercial-scale operations more important to realize this protection.

It is also important not to allow the volatiles in the petroleum coke to get too high since they provide heat to a kiln system with an oxidizing off gas and, if too high, then they make operating an oxidizing kiln more difficult. In addition, the volatiles add hydrogen to the kiln, ultimately producing water that limits the strength of phosphoric acid that can be made from the process. However, green petroleum coke with less than 12 wt % volatiles may be suitable for use in the KPA process. Reduction in carbon burnout with increasing kiln diameter due to the sweep effect of the volatile gases multiplies the reduction in carbon burnout with increasing kiln diameter due to the surface area limitation of oxidizing gas transport to the bed, thus giving compounded lowering of carbon burnout with kiln scale up.

The evolving hydrocarbons from the kiln bed may have another direct effect on the reduction of carbon burnout from the kiln bed. The volatile hydrocarbons may react with the oxidizing gases from the freeboard in a way that creates a product which is not reducible by the carbon in the kiln bed. Consider the following reaction:

CH₄(from bed)+CO₂(from freeboard)->CO+2H₂

Neither of the reaction products is reducible by the carbon in the bed. As a result, the hydrocarbon not only sweeps the oxidizing gasses away from the bed, but also intercepts the remaining oxidizing gases and transforms them into nonoxidizing gases. Note that this effect is also directly related to the surface/volume ratio in the kiln bed and multiplies the reduction in carbon burnout fraction by the two mechanisms discussed above.

Even though the use of uncalcined carbonaceous material evolves volatiles effective in substantially reducing carbon burnout in large enough kilns, its evolution from the bed is largely complete at 950° C., leaving the bed largely unprotected between 950 and 1180° C., where the phosphate ore reduction reaction proceeds at a reasonable rate. In order to minimize the carbon burnout during that interval, incoming kiln solids may be heated to reaction temperature as rapidly as possible.

Special provisions may be made to rapidly heat up the kiln solids. The KPA process is unusual in that essentially all of the fuel required to heat the kiln and feed agglomerates and provide the heat for the endothermic phosphate reduction reaction is generated as a result of the reduction reaction itself. The reaction forms phosphorus metal and carbon monoxide off gases according to the reaction:

Ca₁₀(PO₄)₆F₂+9SiO₂+15C->3/2P₄(gas)+15CO(gas)+9CaSiO₃+CaF₂

The combustion of the carbon monoxide and phosphorus metal from the reduction reaction, the burning of coke volatiles, and the oxidation of some of the carbon from the bed generates all the heat necessary for the KPA process. Nevertheless, the heat must be distributed down the kiln to be effectively used. The hot combustion gases that result from the burning of phosphorus and carbon monoxide do not have sufficient latent heat to supply the endothermic needs of the phosphate reduction reaction. Therefore, previous attempts by Hard, Megy, etc. to run the KPA process by passing air entirely into the burner end of the kiln resulted in runaway temperatures over a small length of the kiln near the burner.

Such a runaway reaction occurred in the continuous kiln pilot plant of the Leder article discussed in the Background section above and not only limited its performance, but forced it to be operated at high silica feed formulations, reducing off gas, and a high temperature peak near the burner end. Together with modest yields, the processing restrictions resulted in lowered commercial prospects for the process. One means to spread the heat generated by the burning of the phosphorus metal gas and carbon monoxide down the kiln is to limit the amount of oxygen present at the site of the reaction near the burner. Limiting oxygen leaves phosphorus and carbon monoxide in the freeboard which is then burned with cold air from over bed air ports as needed to supply an even temperature down the kiln.

Ported kilns are not common, but have been used previously in several commercial kiln processes to supply over bed air for down kiln combustion or place air or other gases under the bed as a reactant. Using a ported kiln to supply controlled over bed air to the KPA process allows the temperature to be held at an optimum temperature profile for forwarding the phosphate reduction reaction over most of the kiln length and to bring the incoming kiln solids rapidly up to reaction temperature. By reducing the time the kiln feed agglomerates spend in reaching reaction temperature the carbon burnout may be reduced. As discussed below in relation to FIG. 1, a control system may be implemented to achieve the desired effects of over bed air addition.

Several other benefits accrue to the establishment of a long reaction zone at a just sufficient minimum kiln bed temperature, including: much improved processing rates due to the longer reaction times for heat transfer, longer refractory life, reducing clinker formation and refractory-kiln solids interactions, eliminating sinoite formation, and minimizing the loss of sulfur, sodium, potassium, and fluorine from the bed.

As a result of the research described herein, it was newly discovered that the sinoite reaction occurs during the operation of the KPA process if run at higher temperatures. The reaction of nitrogen from the freeboard and silica with fixed carbon in the reducing kiln bed competes with the phosphate reduction reaction above 1310° C. Between 1180° C. and 1310° C. the phosphorus reaction occurs, but not the sinoite reaction. If the KPA kiln residue is heated to over 1310° C. after the phosphate ore has been reduced, then the sinoite reaction proceeds, using up any excess carbon. When the carbon is exhausted from the kiln solids residual, it becomes stickier and more difficult to handle. The sinoite does not otherwise help the KPA process, so it is useful to get maximum throughput and discharge the kiln solids from the kiln as soon as the phosphate ore has been reduced.

One additional method of limiting carbon burnout in the KPA kiln includes adding a small amount of loose, small sized pieces of a carbonaceous material together with the raw material feed agglomerates to the KPA kiln. If the kiln has a small enough bed surface/volume ratio and a fast enough feed heat up rate, then small amounts of carbonaceous material at about 1-2% of the weight of the feed agglomerates are sufficient to provide sacrificial carbon burnout throughout the feed agglomerates while heating them to reaction temperature. Such additions of sacrificial carbon outside the feed agglomerates are more effective than adding more carbon to the raw material mixture that make up the agglomerates.

An advantage exists in using uncalcined carbonaceous material since the volatiles therefrom contribute to the volatiles sweep effect and to the reaction with the incoming oxygen flux from the freeboard, decreasing P₄O₁₀ condensation and calcium metaphosphate formation. It is particularly advantageous to use carbonaceous material that evolves some volatiles between 100° C. and 650° C., which limits P₄O₁₀ transfer from the kiln freeboard to the cold raw material agglomerates entering the kiln. The P₄O₁₀ otherwise condenses on the cold feed balls at less than 485° C. and can react with fluorapatite (Ca₁₀(PO₄)₆F₂) to form calcium metaphosphate. Additionally, P₄O₁₀ may react with carbon at about 800° C. Enrichment of feed balls with phosphorous in such manner essentially recycles phosphorous from the back end of the kiln to the front end. Such enrichment accentuates carbon burnout by placing an increased demand on carbon to re-reduce phosphorous in the condensed P₄O₁₀ and/or calcium metaphosphate. Although the slow mass transfer from the kiln freeboard to the bed limits the extent of this occurrence, particularly in larger kilns, it can be further mitigated by the low temperature volatilization of organics from the carbonaceous material.

If the phosphate ore has a suitable organic level it is useful for this purpose. Coal also has low temperature volatile organics that is useful for this purpose. The carbonaceous material may be more effective if sized to small pieces which present maximum surface area to the incoming oxygen flux. The particle size should not be so small that it entrains as dust into the freeboard gases of the kiln. Carbonaceous material in the ¼ inch to ½ inch size range has been found to be effective.

Fine grinding of the carbonaceous material and its effective distribution in the raw material agglomerates may be important to the process. Jacob et al., Reduction of Tricalcium Phosphate by Carbon, I&EC, Vol. 21, No. 11, 1929, 1126-1132 and Mu et al., Thermodynamics and Kinetics of the Mechanism of Reduction of Phosphate Ores by Carbon, Met. Trans. B, 17B, 1986, 861-868 discuss that phosphate reduction with carbon is a first order reaction, but neither describe the effect of carbon surface area on the rate of reaction or the effect of intimate mixing. Observation indicates the rate controlling step in the KPA process is the diffusion of phosphorus and silica molecules across a growing calcium metasilicate layer around each carbon particle. As the layer thickens, the reaction slows down, giving the known first order reaction rate behavior.

Grinding the carbon finer not only gives a higher surface area for a given weight of carbon, but also decreases the distance between the carbon particles. Thus, the diffusion path to the carbon particles is shortened for the phosphate and silica. Based on the research data described herein, it was newly discovered that the carbon particle diameter shrinks as it reacts, resulting in a void between the carbon and the phosphate ore/silica that may add extra resistance to phosphate reduction when the carbon particle size is greater than 200 mesh. With such larger sized carbon particles, a slower reaction rate exists due to a lower specific surface area. Also, the added distance between particles results in a logarithmic increase in the time it takes at a given temperature to consume all the phosphate between the particles.

Intimate mixing of the carbon ensures realization of the advantageous diffusion characteristics and may be efficiently accomplished by co-grinding the raw materials. Otherwise, carbon particles, even though smaller, may clump together and provide less benefit since a clump of small particles functions like a single large particle. Maintaining a higher reaction temperature can increase the phosphate/silica diffusion rate to overcome a lack of mixing or a larger carbon particle size. However, the higher reaction temperature may reduce kiln throughput, increase volatilization of bed impurities, increase carbon burnout, lead to reduced refractory life, and create other problems. Observation indicates that open-circuit ground green petroleum coke, 80 wt % of which exhibits a size less than 200 mesh, providing an amount of fixed carbon 1.3 times a theoretical carbon requirement for reduction of all phosphate in the ore can carry out over 95% phosphate reduction in less than two hours when intimately mixed in the agglomerates. However, over 95% phosphate reduction takes over six hours if −140/+200 mesh coke is used instead. “Open circuit” grinding refers to batch grinding until a charge of material meets specification as opposed to “closed circuit” where material meeting specification is continuously removed and other material remains for further grinding. Open circuit grinding thus generates more fines.

According to another aspect of the invention, a phosphorous pentoxide producing method includes forming a kiln bed using feed agglomerates in a counter-current rotary kiln, the bed having a length and the agglomerates containing phosphate ore particles, carbonaceous material particles, and sufficient silica particles for the agglomerates to exhibit a calcium-to-silica mole ratio of less than 1.0. Individual agglomerates substantially exhibit a same elemental composition, a same calcium-to-silica mole ratio, and a same proportion of excess fixed carbon compared to a theoretical carbon requirement for reduction of all phosphate in the ore. Co-grinding and other concepts described herein may provide such agglomerates. The method includes maintaining a bed temperature at or above 1180° C. along a portion of the bed length and establishing a bed surface-to-volume ratio multiplied by a time for bed heat up to 1180° C. of less than 50 minutes-ft²/ft³ to obtain a yield of greater than 90%.

By way of example, the bed temperature may be maintained at or above 1260° C. along at least 50% of the bed length. Maintaining the bed temperature may include not exceeding 1380° C. along the entire bed length. The method may further include blanketing the bed with volatiles evolving from the carbonaceous material during bed heat up from about 600 to about 950° C. Also, the kiln bed may include, initially, from about 1 to about 2 wt % bedding coke or coal. Such bedding may blanket the bed with volatiles evolving from the bedding coke or coal during bed heat up from about 100 to about 650° C.

Over bed air and/or oxygen may be added through a plurality of ports along the bed length, the ports being of sufficient location, number, and throughput to decrease a time for bed heat up to 1180° C. compared to otherwise identical processing without the over bed air and/or oxygen. Control systems may provide for monitoring of temperature at an inner surface of the kiln at a plurality of points along the bed length, the inner surface contacting the bed, and also monitoring oxygen and carbon monoxide content of the kiln off gas. Further monitoring of carbon dioxide content may provide a check against the values obtained for oxygen and carbon monoxide content.

The Lapple and Megy patents introduced in the Background section specify a calcium-to-silica mole ratio greater than 1.0. However, observation indicates that a eutectic composition between the calcium metasilicate product from the reduction reaction and unreacted fluorapatite arises part way through the reduction step in such processes and results in melting problems in attempts to carry out such processes in rotary kilns. It is believed that all attempts to carry out the KPA process with calcium-to-silica mole ratios greater than 1.0 cannot be successful unless implementing very high calcium-to-silica ratios, as taught in the Park patent. Consequently, the aspects of the invention herein are advantageously limited to a ratio less than 1.0.

FIG. 1 shows a block diagram demonstrating process flow for the KPA process. A range of phosphate ores can be processed by the KPA process by adjusting the raw material composition to accommodate the impurity level therein. For example, if the raw material mixture contains less than about 1.5 wt % Al₂O₃, then silica admixtures may be processed with calcium-to-silica mole ratios approaching 1.0. On the other hand, if ores up to about 3 wt % Al₂O₃ are processed, then the calcium-to-silica ratio may be less than 0.5 to reduce melting problems in the kiln and provide enough temperature window for commercial operation. No need exists to remove fines from the ore. Some fines are beneficial in forming strong agglomerates for the KPA process. If washed ore is used for impurity control or to reduce moisture in the feed ore, then bentonite or other clay additions to the raw material mixture help to make sufficiently strong balls.

The amount of silica added also affects the overall heat balance of the kiln. Greater than stoichiometric amounts of fixed carbon are used to fully reduce the phosphate ore in the KPA process. The phosphate ore reduction produces a stoichiometric amount of phosphorus metal vapor and carbon monoxide fuel. Thus, the KPA process tends to develop more than enough heat to be utilized in the kiln with an oxidizing off gas. Additional silica in the mixture uses up some of the heat albeit at the expense of additional grinding and handling costs.

Phosphate ore deposits, as mined, frequently have sufficient silica content to meet the requirements of the KPA process. Sometimes a mixture of the washed and unwashed ore is used to provide sufficient clays for binder, but some clay removal may occur to meet the desired aluminum level for a given silica addition level. Potassium and sodium level in the ore can be a problem if at unusually high levels. Iron impurities may reduce yield by combining with phosphorus to form a ferrophosphorus alloy which stays in the kiln residue. At levels normally found in the US phosphate ore deposits, iron reduces yield to phosphorus oxide in the off gas by 1.5-3%.

In some cases it may be economically advantageous to use phosphate ore with pebble phosphate rock removed for other uses and the remaining silica, phosphate rock mixture beneficiated by fatty acid floatation to adjust silica level. High moisture levels in the as mined phosphate ore mixture that are expensive to dry may affect raw material selection for the process. Clay added to the process usually contains high associated moisture levels, but usually has a particle size distribution largely under 200 mesh. Thus, the clay need not be ground and wet clay can be added to the other dry ground raw materials, also supplying the water required in the agglomeration or balling operation. Such measure reduces the overall drying requirements when wet clay is the binder.

The selection of the phosphate ore to use in the KPA process may be made to minimize its cost. If one mine serves both KPA and dihydrate phosphoric acid production plants, then additional options are available in selecting phosphate ore from one of the partially beneficiated steams as a component of the KPA raw material mixture.

In dry ore deposits, the phosphate ore feed to the KPA process may be as mined phosphate ore matrix. Part of the matrix may warrant washing if the Al₂O₃ concentration is too high and silica additions may be desired if the ore does not contain enough silica.

Sufficient carbonaceous material may be added to the phosphate ore to result in fixed carbon content in the raw material mixture of about 1.3 times the theoretical carbon required to reduce the phosphate contained in the raw material mixture. The volatile content of the carbonaceous material may be limited to less than 12 wt % to achieve a favorable heat balance in the KPA process kiln (maintaining an oxidizing off gas) and to limit hydrogen addition to the raw materials. The level of hydrogen input to the kiln limits the maximum concentration of phosphoric acid that can be made in the KPA process. Green petroleum coke may be used as the carbonaceous material with volatiles in the 8-10 wt % range, where they are high enough to offer protection against carbon burnout in larger kilns, but not so high that hydrogen additions interfere with producing 72-76% phosphoric acid from the KPA process.

High sulfur, green petroleum coke may be used in the KPA process since most of the sulfur stays with the kiln residue in an optimally run process. With power production as the main alternative use for petroleum coke, high sulfur petroleum coke is generally cheaper than low sulfur petroleum coke due to the expense of removing sulfur from the stack gas of power plants. While coal may be equally effective for such purposes in the KPA process, only coal with unusually low volatiles has low enough hydrogen levels to curtail heat balance problems and limitation of the concentration of the phosphoric acid product. Alternatively, the coal can be calcined, but then the cost of additional processing becomes a factor.

An example of a suitable raw material feed mixture for a favorable deposit in the US state of Idaho is one part as-mined raw ore matrix which has been processed to remove material larger than 3 inches and 0.09 parts green petroleum coke sized 3 inches and down. To supply a 19 foot diameter (inside the bricks) rotary kiln to make 200,000 short tons per year (P₂O₅ basis) in the form of super phosphoric acid (SPA) requires about 230,000 pounds/hour (lbs/hr) of raw matrix ore and 23,000 lbs/hr green petroleum coke.

In process flow of FIG. 1, the raw materials are analyzed for moisture and metered together to form a raw material mixture then dried to 1.5 wt % moisture in a rotary drier using waste heat from the rotary cooler used later in the process. The dried ore mixture is sized to about ⅜ inch in a crushing/screening circuit and passed into an open circuit dry ball mill for grinding to 80%-200 mesh. Next, 9 wt % moisture is added to the co-ground raw material mixture and the result formed into balls in a balling drum/roller screen circuit with the addition of 3 wt % additional water in the balling drum sprays to control the ball growth. The balls exhibit a greater than ¼ to less than ½ inch (+¼/−½) diameter.

Thereafter, the wet green balls are layered on a perforated stainless steel belt and dried in a low temperature belt drier with waste heat from the kiln spent solids cooler later in the process. Further, 1 wt % (i.e., 2,500 lbs/hr) bituminous coal sized to +¼/−½ inch is added to the wet feed balls as they pass into the continuous belt dryer. The agglomerates/bituminous coal feed leaves the drier at 125° C. and passes into a 19 foot diameter (inside the bricks) rotary kiln.

The kiln of FIG. 1 is a ported kiln equipped with a circumferential channel with a moving seal that passes air from blowers outside the kiln through headers with volume control valves and ports to the inside of the kiln wall where the air is distributed along a channel in the brick and then to the freeboard of the kiln through slits in the brick. Shut off valves on each of the headers are turned on and off during each rotation to pass air into the freeboard only when the ports are above the kiln bed. The Folmo article referenced above describes such a kiln.

However, the kiln of FIG. 1 additionally includes a temperature and off gas control system. The kiln is fitted with on board thermocouples every 6 feet which measure the temperature of the brick about ⅜ inch below the hot surface of the brick. The temperature seen by these thermocouples can be related to the brick surface temperature as measured by an optical pyrometer when the kiln is empty. When the KPA process is operating, the white, opaque phosphorus burning flame obscures the view of an optical pyrometer, which is the common way to determine internal kiln temperatures in other processes. Even so, the temperature data obtained from the thermocouples may be relied upon to control air addition through the ports and, thus, temperature profile along the kiln length.

The kiln feed agglomerates are rapidly heated to 1180° C. by the hot counter currently flowing freeboard gasses and maintained above that temperature over most of the kiln length by adjusting the addition of air along its length to achieve the corresponding onboard brick thermocouple readings. The feed end of the kiln includes a tapered dam to reduce the turbulence associated with a dam commonly used in these kilns to retain solids. Reduction in turbulence at the feed end achieves greater benefit than at the burner end since the calcium metasilicate reaction product encapsulating the carbon particles provides some protection closer to the burner end. A small flame is maintained at the burner to stabilize the front of the kiln and achieve overall heat balance.

An off gas analyzer capable of analyzing CO, CO₂, and O₂ is included and continuously monitored to ensure the kiln maintains a slightly oxidizing off gas. The above air addition control system may maintain the desired kiln temperature profile. However, the off gas analyzer may be used to monitor whether other process changes might be warranted, in keeping with the discussion herein, so that the air added is also sufficient to oxidize all of the P₄ and CO, with O₂ in slight excess.

The hot kiln solids in FIG. 1 pass out of the kiln past an isolation curtain into a rotary cooler. Heat is recovered from the hot balls into an air stream which is used to dry the combined raw materials and the green balls from the balling drum. The cooled balls pass out of the cooler, through an isolation valve to a conveyor belt that removes the spent balls to a disposal site.

The hot gases containing the P₄O₁₀ product exiting the FIG. 1 kiln at about 1100° C. pass through a dust cyclone and then go to a spray tower that contacts the off gas with recirculated, cooled strong phosphoric acid that absorbs about one half of the P₄O₁₀ therein and cools the off gas to about 260° C. The product phosphoric acid (72-76% P₂O₅) is split from this recycle stream. The remaining phosphoric acid is removed from the gases leaving the spray tower in a high pressure drop venturi, which has recirculated, cooled weak phosphoric acid as the scrubbing liquid used as required to make up liquid volume in the spray tower liquid. The product scrubber in FIG. 1 includes the spray tower and venturi and may produce any concentration of P₂O₅ less than or equal to about 76%. However, 72% may be selected because it is at the bottom of a eutectic and remains more fluid at room temperature, albeit still with a relatively high viscosity.

An induced draft (ID) fan pulls the gasses through the kiln and off gas scrubbing system of FIG. 1. The gasses exiting the ID fan are treated with a flue gas desulfurization scrubber to remove acidic components from the off gas before it discharges to the environment.

Example 1

Raw phosphate ore from the Meade formation near Soda Springs, Id. was combined with raw silica ore from a mine near Soda Springs, Id. and delayed green petroleum coke from a gulf coast petroleum refinery such that the calcium-to-silica mole ratio was 0.56 and the fixed carbon in the petroleum coke was 1.3 times the theoretical to reduce the phosphate in the mixture. The mixture contained 13.43 wt % P₂O₅, 21.33 wt % CaO, 42.42 wt % SiO₂, and 7.38 wt % fixed carbon on a dry basis. The mixture was dried and then ground to 80.2%-200 mesh in an open circuit ball mill. Twelve percent water was added to the ground mixture and formed in a die into several ½ inch diameter pellets which were then dried in an oven at 280° F. One pellet was placed in a graphite crucible with a graphite lid and the crucible and its contents heated at 20° C./min to 1180° C. and held for one hour under an atmosphere of nitrogen. After cooling the crucible to room temperature the pellet was analyzed to determine how much phosphorus had evolved from the pellet. The experiment was repeated with the time at 1180° C. increased to two hours and then to four hours. It was found that 61%, 82% and 97% of the phosphorus had evolved from the pellet in 1, 2, and 4 hours at 1180° C., respectively.

Over 100 experiments were additionally performed using the same procedure with a range of temperatures, impurity levels, reaction times, calcium-to-silica mole ratios, grind sizes, and carbon addition levels. Some of the most significant variables are summarized in FIG. 2.

Example 2

Several of the spent pellets from Example 1 were analyzed and compared to the analyses of the feed pellets to determine the fate of impurities in the feed compositions. The elements that volatilized either partially or totally from the pellet during the phosphate reduction together with the weight fraction of the element in the feed pellet, were Ag (<1 ppm), As (10.2 ppm), C (8.2%), Cd (33 ppm), Cl (90 ppm), Cs (1.3 ppm), F (1.27%), Ga (3 ppm), Hg (0.22 ppm), K (0.44%), N (0.13%), Na (0.25%), P (6.55%), Pb (7 ppm), Rb (18 ppm), S (0.73%), Se (6.8 ppm), Tl (1 ppm), and Zn (688 ppm). The elements which were present in significant amounts, which were of concern, and which evolved from the feed pellets were K, Na, S, and F. FIG. 3 shows the weight fraction of these elements which volatilized from the pellet over a range of hold temperatures as compared to the weight of the elements in the feed agglomerates. The composition of the pellets tested in this volatilization study is the same as given in the 1180° C. tests given in Example 1.

Thus, in a fully reducing environment, part of these elements volatilized from the kiln solids. To the extent an oxidizing shell forms from carbon burnout, the loss of these elements is expected to be much higher therein.

Example 3

The co-ground ore/silica/green petroleum coke mixture indicated in EXAMPLE 1 above was blended with 9 wt % moisture and formed into +¼/−½ inch balls on a 3 foot balling pan with an additional 3 wt % moisture added through control sprays on the balling pan. The balls were dried in a tray drier, and a twenty pound charge of balls was processed in a 13.5 inch diameter by 22¼ inch long batch rotary kiln at 1320° C. The kiln was fired with 1 to 2 feet³/minute (cfm) of propane, about 44 cfm of air, and 0 to 2 cfm of oxygen as necessary to hold the temperature at the set point. The kiln was fitted with an onboard thermocouple and had zircon refractories.

The kiln was preheated to 1189° C. and twenty pounds of balls were charged to the batch kiln with a scoop. Samples of the kiln solids were sampled every fifteen minutes and analyzed to determine the burnout of carbon and the extent of phosphate reduction. The surface of the kiln bed reached 1271° C. by the minute sample, overshot to 1332° C. by the 30 minute sample, and was 1320° C. for the 45 minute sample. The carbon content of the entering ball was 8.75%, but the sum of volatiles and carbon that reacted with iron oxide and carbonate during heat up was estimated at 0.96% leaving 1.56 pounds of fixed carbon in the 20 pound charge to the furnace. The amount of phosphorus that had evolved, the carbon which had burned out, and the carbon remaining in the balls is given for the three samples in Table 2.

TABLE 2 Carbon burnout and phosphorus evolved from 13.5 inch batch kiln test. Sample P evolved C Reacted C Burnout C Remaining 15 minute 10%  8% 49% 43% 30 minute 27% 21% 62% 17% 45 minute 29% 23% 75%  2%

From this data 62% of the fixed carbon that was in the ball was burned out by oxidizing gasses in 16 minutes as the bed solids heated from 700° C. to 1180° C. where the phosphate reduction reaction commenced. The surface area of the bed was 1.69 square feet and the volume of the bed was 0.28 cubic feet. Therefore the carbon burnout rate was 3.46 pounds per hour per square foot, and the heat up time times the surface-to-volume ratio is equal 97 min-ft²/ft³.

The twenty pounds of feed agglomerates charged to the kiln contained green petroleum coke with 0.19 pounds of volatiles. Since these volatiles emerged from the bed over about a fifteen minute period, their flux was about 0.45 pounds per hour per ft². The phosphorus and carbon monoxide gases from the run were 29 wt % of the total phosphate ore mass charged to the batch kiln and totaled 0.67 pounds over about twenty minutes or about 1.19 pounds per hour per ft². The carbon burnout and phosphate reduction were occurring so rapidly with regard to the 15 minute samples in the very small batch kiln that the protective effect of the volatiles from the green coke was not sufficient to be clearly observed. Nevertheless, the existence of a protective effect of the phosphorus metal and carbon monoxide was suggested in the data from this test.

Samples of the product balls after 45 minutes in the kiln were split in two and a white shell and black core with a sharp boundary between them was observed. The thickness of the shell was measured at a number of points around the circumference on several different balls to obtain an average thickness. From these measurements and the diameter of the ball, the volume fraction of the shell with the carbon burned out was determined to be 70%, and quite consistent over several balls. The shell was determined to contain silica, Ca₃(PO₄)₂, and an amorphous phase likely to be calcium metaphosphate. The phosphorus in the shell was analyzed at 22.5 wt %, which is considerably enriched over the starting phosphorus level in the feed ball. The core contained less than 1 wt % residual phosphorus. The shell composition indicated the reaction of phosphorus metal in the shell or the area between the balls with oxidizing gases from the freeboard, forming P₄O₁₀ which, in turn, reacted with fluorapatite in the shell to form the amorphous phase. Table 3 lists analyses of the feed ball, shell, and core.

TABLE 3 Analysis of the core and shell from the 45 minute sample in batch kiln test of Example 3. Component Feed Ball Core Shell P₂O₅ 13.95%   0.3%*  20.7% CaO 20.16% 23.25% 18.42% MgO 0.279% 0.324% 0.240% SiO₂  24.6% 42.33% 35.34% K₂O 0.326% 0.390% 0.149% F  1.54% 0.647% 0.057% S 0.783% 0.488% 0.022% *From XRD analysis.

Example 4

A mixture of washed, but not beneficiated phosphate ore matrix direct from a Florida phosphate mine and calcined petroleum coke with an analysis of 11.0% P₂O₅, 15.9% CaO, 56.2% SiO₂, and 11.4% fixed carbon respectively, was ground to 80%-325 in a dry ball mill and formed into balls using a balling pan. These balls had a calcium-to-silica mol ratio in the feed of 0.304 and fixed carbon at 2.45 times the theoretical amount to reduce the phosphate ore therein. The dried balls were passed into a 33 inch diameter (inside the bricks) by 30 foot long counter-current kiln at 600 pounds per hour, ultimately reaching a bed temperature of 1520° C. near the burner end of the kiln at the furthest point into the kiln that could be observed with an optical pyrometer. The dense, white flame of burning phosphorus obscured making temperature measurement further into the kiln.

During the continuous kiln operation, the kiln was stopped briefly and samples of kiln solids were taken at the discharge of the kiln and with a long probe at 3¾ foot, 7½ feet, 13¼ feet, and 15 feet from the hot end of the kiln. The samples were analyzed for carbon, calcium, and phosphorus. The percent of phosphorus and carbon volatilized, the mass (lbs/hr) of carbon consumed in the phosphorus reduction (C(P rx)), and the mass (lbs/hr) of carbon burned out (CBO) at each sample location was calculated with the results shown in Table 4.

TABLE 4 Analytical data from continuous KPA pilot plant run. Dist from % P % C lbs C lbs Feed loss loss (P rx)/hr* CBO/hr Feed 0 0 0 0   15 feet 2 20.2 0.6 13.3 18.75 feet 10 35.7 2.8 21.6  22.5 feet 49 52.6 13.7 22.3 26.25 feet 65 58.6 18.1 22.0   30 feet 72 61.4 20.1 21.9 *This is the amount of carbon in pounds/hr that was consumed by reacting to reduce phosphate ore within the ball.

The kiln was not ported and all of the oxygen required to oxidize the phosphorus and carbon monoxide arising from the bed was burned with air added at the burner end of the kiln. The observed position where phosphorus was volatilized given in Table 4 showed that most of the phosphorus and carbon monoxide were generated and burned over a narrow length of the kiln at the burner end of the kiln. Thus, a narrow temperature spike occurred with the peak temperature of 1520° C. to get the 72% phosphorus yield during the short time duration of the temperature spike. The kiln overall had an off gas that was reducing, meaning that it contained no excess oxygen. Typically, reducing off gas thus contains unoxidized CO and may even contain some unoxidized P₄.

The kiln solids had a relatively long heat up time where the kiln solids were between 700° C. and 1180° C., during which time carbon was burned out of the shell. The calcined petroleum coke used in the feed formulation did not evolve any volatiles to protect the kiln bed during heat up. However, once significant generation of the phosphorus metal and carbon monoxide evolved from the kiln solids commenced about 19 feet into the 30 foot kiln, the rate of carbon burnout was essentially stopped as shown in the lbs CBO/hr column of Table 4.

The amount of phosphorus and carbon monoxide which evolved per hour in the kiln was 40.8 pounds per hour, which evolved over about a 6 foot length of the kiln in which the solids spent about 30 minutes and which had a bed surface area of 13.37 ft². In this case the resulting flux of 6.1 pounds per hour per square foot substantially limited oxidizing gas transport to the bed and essentially stopped carbon burnout during the period of phosphate reduction. The product calcium metasilicate glassy residue also encapsulated the remaining carbon and helped protect it from carbon burnout.

The spent balls that exited the kiln were broken in half and observed to have a white shell and a black interior with a sharp line of demarcation between the two areas. The white shell had no fixed carbon and high levels of phosphorus remaining. The black core had phosphorus reduction of over 96% and carbon remaining in the core.

The heat up time of the bed from feed temperature to 1180° C. was about 2.23 hours, which gives a bed surface-to-volume ratio times heat up time value of 334 minutes-ft²/ft³. The carbon burnout rate during heat up was 0.272 pounds per hour per square foot.

Hypothetical Example 5

The observations made in the preceding examples allow calculation of the performance of a full scale commercial KPA kiln run according to the various aspects of the invention. Kiln feed balls made from raw matrix ore with calcium-to-silica mole ratio of 0.5 and a fixed carbon content of 1.3 times the theoretical amount to reduce the phosphate in the ore are made by combining 1 part raw matrix phosphate ore with 15% contained P₂O₅ from the Mead formation in Idaho, trammeled to remove +3 inch oversize material, and 0.09 parts green petroleum coke sized 3 inch and less. This mixture is dried in a rotary drier, sized to ⅜ inch and less and co-ground in an open circuit ball mill to 80%-200 mesh. The ground ore is formed into +¼/−½ inch balls on a balling drum which are dried in a grate drier. One and a half percent coal sized to +¼/−½ inches is added to the balls prior to the grate drier.

This feed is processed at the rate of 490,000 pounds per hour in a 19 foot diameter (inside the bricks) by 220 foot long rotary kiln equipped with a porting system to supply over bed air as required to provide the desired temperature profile, on board brick thermocouples, and an off gas analyzer capable of analyzing CO, CO₂, and O₂. The loading in the kiln is 15% and the kiln burden spends one and one/half hour in the kiln. It is heated to 1260° C. in 30 minutes and the temperature held at 1260° C. until the solids discharge from the kiln one hour later. The bed volume is 9,945 ft³ and the bed surface area is 3,600 ft².

The coal which has 25% volatiles which produces about 880 pounds per hour of volatiles while the incoming kiln feed mixture is heated from an entering temperature of 125° C. to 600° C. which occurs in 10 minutes. Thus, the flux of hydrocarbons in the cold end of the kiln is 2.3 pounds per hour per ft², which by comparison with the phosphate reduction flux that provided protective above, is sufficient to give a modest protective effect to prevent P₄O₁₀ from the freeboard from condensing on the cold balls.

Heating the balls from 600° C. to 950° C. takes another 10 minutes. During this time the volatiles from the green petroleum coke and the coal total 4,480 pounds providing a protective flux of 45 pounds per hour per square foot. In addition, the light molecular weight of the volatiles and their ability to react with the incoming oxidizing gases make them more effective than phosphorus metal and carbon monoxide fluxes which were found to be effectively protective at a flux one ninth as great in Example 4.

During heating from 950° C. to 1180° C. which takes an additional 10 minutes the balls are subject to carbon burnout at a rate of about 1 pound per hour per square foot over 1660 square feet or about 1660 pounds per hour of carbon burnout. The sacrificial carbon intercepts about 40% of the incoming oxidation so the fixed carbon burned out of the balls is about 1000 pounds per hour or about 1/40th of the fixed carbon in the incoming balls. This results in the carbon being burned out of a thin shell on the outside of the feed balls which is not reduced after the balls reach reaction temperature. Thus a loss in yield of just over 2% results from carbon burnout in this area.

The bed volume to surface area ratio times the heat up time in this commercial kiln is 11 minutes-ft²/ft³.

After the balls reach 1180° C. until they discharge from the end of the kiln a total of 98% of the phosphate ore is reduced giving rise to 91,800 pounds per hour of phosphorus metal and carbon monoxide flux through 6,630 square feet of bed or a flux of 13.8 pounds per hour per square feet ore several times the flux found in Example 4 to be substantially protective against carbon burnout. During this time the fixed carbon from the coal on the outside of the balls and the carbon rich core inside the ball allow some reduction of phosphorus in the shell, mitigating somewhat the loss of yield from carbon burnout in the shell. Three percent of the phosphorus that forms remains in the bed in the form of ferrophos due to the relatively high amount of iron found in matrix ore.

Since the carbon burnout is now at a low level the reduction of the phosphate in the balls can be allowed to take place at an optimum temperature which is sufficient to react the phosphate during the one hour dwell time in the hot zone of the kiln, but low enough to reduce the loss of sodium, potassium, fluorine, and sulfur to the freeboard while the phosphorus is removed from the kiln residue. Operation at this relatively low temperature, but over an extended length of the kiln, also gives high throughput, long refractory life, freedom from problems associated with melting in the kiln burden, and freedom from problems associated with sinoite formation in the kiln. The relatively low overall carbon burnout allows operation of the kiln with an oxidizing off gas so that an afterburner is avoided.

Thus, this example provides a process wherein relatively cheap green petroleum coke provides the reactant and heat to produce high quality phosphoric acid product (72-76% P₂O₅) at the rate of 523,000 pounds P₂O₅ per hour from as mined matrix ore and to produce a kiln residue that is insoluble and can be used for landfill.

According to a further aspect of the invention, a phosphorous pentoxide producing method includes forming a kiln bed using feed agglomerates and, initially, from about 1 to about 2 wt % bedding coke or coal in a counter-current rotary kiln, the bed having a length and having a surface-to-volume ratio of less than about 1.15 ft²/ft³ and the kiln having an inner diameter of at least about 6 feet. The agglomerates contain phosphate ore particles, carbonaceous material particles containing from about 8 to about 12 wt % volatiles, and sufficient silica particles for the agglomerates to exhibit a calcium-to-silica mole ratio of from 0.5 to less than 1.0, at least about 80% of all particles exhibiting a size less than 200 mesh. Individual agglomerates substantially exhibit a same elemental composition, a same calcium-to-silica mole ratio, and a same proportion of excess fixed carbon at least about 1.3 times a theoretical carbon requirement for reduction of all phosphate in the ore.

The method includes maintaining the bed surface-to-volume ratio with an inlet dam sufficiently tapered such that it reduces turbulence compared to otherwise identical processing with an untapered dam. The method also includes adding over bed air and/or oxygen through a plurality of ports along the bed length, the ports being of sufficient location, number, and throughput to decrease a time for bed heat up to 1180° C. compared to otherwise identical processing without the over bed air and/or oxygen. The method further includes maintaining a bed temperature at or above 1180° C. along at least 50% of the bed length without exceeding 1310° C. along the entire bed length. The method still further includes generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas, the kiln discharging a residue containing processed agglomerates, less than 10% of the agglomerates' phosphate input to the kiln remaining in the residue as phosphate. By way of example, less than 5% of the input phosphate might remain in the residue. Calculation of the maximum surface-to-volume ratio for this aspect of the invention assumes a kiln length of 72 ft and a solids loading of 15%. Generally, the aspect ratio of the kiln may be about 12 or less (i.e., 6 ft diameter×12=72 ft). The various aspects of the invention herein may allow for a ratio as low as about 10.

Features described herein associated with other aspects of the invention may be useful with the present aspect of the invention.

The various aspects of the invention may make a high purity phosphoric acid that can be produced at 76% P₂O₅ content and may vary to as low as 72%. Such KPA product may be similar to a SPA product made by concentrating merchant grade acid (54% P₂O₅) from a wet acid process by further evaporation to a similar concentration, albeit with a lower purity level in the evaporation product. At 72% P₂O₅, the SPA has less ability to yield sludge from the impurities and can be used to make various liquid fertilizers by the addition of ammonia to produce MAP and/or DAP.

The liquid fertilizer grades also do not contain sludge and can be added directly to water in a farmer's irrigation system in frequent small doses that match the demand of the crop for fertilizer. This practice, called “fertigation”, allows much higher yield in transfer of phosphate and nitrogen to the crop compared to solid fertilizer applications, which are typically made once or twice per season. Fertigation allows much higher yield particularly when the water application is carefully matched to the demand of the crop. Even though products from SPA sell for a premium compared to solid fertilizers, liquid fertilizers generally offer a cheaper overall cost advantage to the farmer when efficiency and yield considerations are taken into account.

Commercial granulated fertilizer products cannot be utilized in fertigation since dissolving them in water results in thick sludge that plugs up irrigation systems. Nevertheless, from a practical standpoint, solid granulated fertilizers are the only fertilizer products that can be transported to overseas customers. Thus, the benefits of fertigation are generally not available to the farmers of third world countries without a phosphoric acid industry.

One method of improving solid fertilizers from the wet acid process may use the high purity, SPA-strength phosphoric acid available from the aspects of the invention described herein. Such a KPA product may be added directly to 26% filtered phosphoric acid or 42% concentrated and filtered phosphoric acid to make a higher purity 54% feedstock for producing granulated fertilizers without further evaporation, saving on evaporation cost. The mixing of the products may also increase the value of 26% or 42% phosphoric acid with too much magnesium by avoiding discounting of fertilizers made from low purity feedstock. Similarly, the high purity KPA product may be used instead of or in addition to lower purity SPA evaporation product to make higher purity liquid fertilizer.

A further approach includes making crystalline MAP or DAP-type products by adding ammonia to the KPA product in a crystallizer rather than a granulator. Crystallizers differ from granulators in that they produce a crystalline product instead of the amorphous solid produced by granulators. In both types of device, heat released from reaction with ammonia may assist in processing. Examples of crystallizers include those described on pages 19-35 to 19-39 of Perry's Chemical Engineers' Handbook, (Don W. Green ed., 6th ed. 1984). The crystalline material from the high purity KPA product may dissolve readily in water without leaving a residue to plug irrigation systems, thereby offering the advantages of fertigation, particularly to overseas customers.

Consequently, aspects of the inventions described herein may further include producing a phosphate-containing fertilizer using phosphorous pentoxide collected from kiln off-gas. Producing the fertilizer may include producing a crystalline solid, for example, by using a crystallizer. The collected phosphorous pentoxide may be comprised by a first product exhibiting a first concentration of phosphorous pentoxide, for example, 72-76%. Producing the fertilizer may include mixing the first product with a second product exhibiting a lower concentration of phosphorous pentoxide. The first and second product mixture may form a third product exhibiting a concentration of phosphorous pentoxide between the first and second products' concentrations and an amorphous solid may be produced from the third product.

In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents. 

1. A phosphorous pentoxide producing method comprising: forming a kiln bed using feed agglomerates in a counter-current rotary kiln, the bed having a length; the agglomerates containing phosphate ore particles, carbonaceous material particles, and sufficient silica particles for the agglomerates to exhibit a calcium-to-silica mole ratio of from 0.5 to 1.0; maintaining a bed temperature at or above 1260° C. along a portion of the bed length without exceeding 1380° C. along the entire bed length; and generating kiln off gas from the portion of the bed at or above 1260° C. and collecting phosphorous pentoxide from the kiln off gas, the kiln discharging a residue containing processed agglomerates, less than 10% of the agglomerates' phosphate input to the kiln remaining in the residue as phosphate.
 2. The method of claim 1 wherein the agglomerates comprise phosphate ore particles, carbonaceous material particles, and silica particles co-ground together.
 3. The method of claim 1 further comprising: adding over bed air through a plurality of ports along the bed length, the ports being of sufficient location, number, and throughput to supply a more even temperature along the portion of the bed at or above 1260° C. compared to otherwise identical processing without the over bed air.
 4. The method of claim 1 further comprising producing a phosphate-containing fertilizer using the collected phosphorous pentoxide.
 5. A phosphorous pentoxide producing method comprising: co-grinding a mixture containing phosphate ore, carbonaceous material, and silica and forming feed agglomerates from the co-ground mixture; forming a kiln bed using the feed agglomerates in a counter-current rotary kiln, the bed having a length; the agglomerates containing phosphate ore particles, carbonaceous material particles, and sufficient silica particles for the agglomerates to exhibit a calcium-to-silica mole ratio of less than 1.0; maintaining a bed temperature at or above 1180° C. along a portion of the bed length without exceeding 1380° C. along the entire bed length and establishing a bed surface-to-volume ratio multiplied by a time for bed heat up to 1180° C. of less than 50 minutes-ft²/ft³; and generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas.
 6. The method of claim 5 wherein the kiln discharges a residue containing processed agglomerates, less than 10% of the agglomerates' phosphate input to the kiln remaining in the residue as phosphate.
 7. The method of claim 5 wherein individual agglomerates substantially exhibit a same elemental composition, a same calcium-to-silica mole ratio, and a same proportion of excess fixed carbon compared to a theoretical carbon requirement for reduction of all phosphate in the ore.
 8. The method of claim 5 wherein the carbonaceous material comprises green petroleum coke particles and, before being co-ground with the ore and the silica, at least about 80% of all green petroleum coke particles comprised by the carbonaceous material exhibit a size less than 200 mesh.
 9. The method of claim 5 wherein establishing the bed surface-to-volume ratio multiplied by bed heat up time comprises further providing a kiln configuration, a bed volume and composition, and kiln process conditions sufficient, in combination, for the kiln to exhibit the ratio.
 10. The method of claim 5 comprising maintaining the bed temperature at or above 1260° C. along at last 50% of the bed length without exceeding 1310° C. along the entire bed length.
 11. The method of claim 5 further comprising blanketing the bed with volatiles evolving from the carbonaceous material during bed heat up from about 600 to about 950° C.
 12. The method of claim 5 wherein the kiln bed further comprises, initially, from about 1 to about 2 wt % bedding coke or coal and the method further comprises blanketing the bed with volatiles evolving from the bedding coke or coal during bed heat up from about 100 to about 650° C.
 13. The method of claim 5 further comprising maintaining the bed with an inlet dam sufficiently tapered such that it reduces turbulence compared to otherwise identical processing with an untapered dam.
 14. The method of claim 5 further comprising: adding over bed air and/or oxygen through a plurality of ports along the bed length, the ports being of sufficient location, number, and throughput to decrease a time for bed heat up to 1180° C. and to maintain a more even temperature along the portion of the bed at or above 1180° C. compared to otherwise identical processing without the over bed air and/or oxygen.
 15. The method of claim 5 further comprising: monitoring temperature at an inner surface of the kiln at a plurality of points along the bed length, the inner surface contacting the bed; adding over bed air and/or oxygen through a plurality of ports along the bed length; and controlling addition of over bed air and/or oxygen based at least on the temperature monitoring.
 16. The method of claim 5 further comprising: monitoring oxygen and carbon monoxide content of the kiln off gas; adding over bed air and/or oxygen through a plurality of ports along the bed length; and controlling addition of over bed air and/or oxygen based at least on the oxygen and carbon monoxide monitoring.
 17. The method of claim 5 further comprising producing a phosphate-containing fertilizer using the collected phosphorous pentoxide.
 18. The method of claim 17 wherein producing the fertilizer comprises producing a crystalline solid.
 19. The method of claim 17 wherein the collected phosphorous pentoxide is comprised by a first product exhibiting a first concentration of phosphorous pentoxide and producing the fertilizer comprises: mixing the first product with a second product exhibiting a lower concentration of phosphorous pentoxide; the first and second product mixture forming a third product exhibiting a concentration of phosphorous pentoxide between the first and second products' concentrations; and producing an amorphous solid from the third product.
 20. A phosphorous pentoxide producing method comprising: forming a kiln bed using feed agglomerates and, initially, from about 1 to about 2 wt % bedding coke or coal in a counter-current rotary kiln, the bed having a length and having a surface-to-volume ratio of less than about 1.15 ft²/ft³ and the kiln having an inner diameter of at least about 6 feet; the agglomerates containing phosphate ore particles, carbonaceous material particles containing from about 8 to about 12 wt % volatiles, and sufficient silica particles for the agglomerates to exhibit a calcium-to-silica mole ratio of from 0.5 to less than 1.0, at least about 80% of all particles exhibiting a size less than 200 mesh; individual agglomerates substantially exhibiting a same elemental composition, a same calcium-to-silica mole ratio, and a same proportion of excess fixed carbon at least about 1.3 times a theoretical carbon requirement for reduction of all phosphate in the ore; adding over bed air and/or oxygen through a plurality of ports along the bed length, the ports being of sufficient location, number, and throughput to decrease a time for bed heat up to 1180° C. compared to otherwise identical processing without the over bed air and/or oxygen; blanketing the bed with volatiles evolving from the bedding coke or coal during bed heat up from about 100 to about 650° C.; blanketing the bed with volatiles evolving from the carbonaceous material during bed heat up from about 600 to about 950° C.; maintaining a bed temperature at or above 1180° C. along at least 50% of the bed length without exceeding 1310° C. along the entire bed length; and generating kiln off gas and collecting phosphorous pentoxide from the kiln off gas.
 21. The method of claim 20 wherein the kiln discharges a residue containing processed agglomerates, less than 10% of the agglomerates' phosphate input to the kiln remaining in the residue as phosphate.
 22. The method of claim 20 wherein the carbonaceous material comprises green petroleum coke.
 23. The method of claim 20 comprising maintaining the bed temperature at or above 1260° C. along at least 50% of the bed length.
 24. The method of claim 20 further comprising: monitoring temperature at an inner surface of the kiln along the bed length, the inner surface contacting the bed; monitoring oxygen, carbon monoxide, and carbon dioxide content in the kiln off gas; and controlling the addition of over bed air and/or oxygen based at least on the oxygen, carbon monoxide, and carbon dioxide monitoring and the temperature monitoring.
 25. The method of claim 20 further comprising producing a phosphate-containing fertilizer using the collected phosphorous pentoxide. 